Xiamen Ji Yuan Stone Co.,Ltd.
Grey Quartz Vanity Top
Grey Quartz Vanity Top
The Grey Quartz Vanity Top is a stunning addition to any bathroom. Crafted from durable grey quartz, it offers both style and functionality. With its sleek design and expert craftsmanship, this vanity top is a perfect choice for your next bathroom renovation. Upgrade your space with the Grey Quartz Vanity Top.
| Feature | Details |
|---|---|
| Material | 93% quartz powder, 7% resin and pigment. |
| Standard Size |
|
| Thickness | 12mm; 15mm; 18mm; 20mm; 30mm |
| Color |
|
| Usage | Slab, Countertop, Kitchen top, Vanity top, island top, Tabletop, Floor, Wall tile, Decorative Borders, threshold, windows sill, tub surround, shower tray and so one |
| Product feature |
1)The product is very hygienic 2)Resistant to scratch,wear,shock. 3)Excellent heat resistance,corrosion resistance. 4)Easy to clean and maintain 5)Anti-Depigment,Anti-penetration,Anti-Porous 6)Environmental friendly building materials. |
| Dimensional Stability | A grade |
| Certificate |
1)The Biggest and leading Group in China. 2) Passed certification of CE and ISO9001:2000 |
| Package | Wooden bundles, wooden crates and wooden cases, plywood case |
| Delivery time | Within 10-15 days after received 30% deposite |
The quality of the quartz stone itself is one aspect. In the process of processing and installation, if there are cutting corners and not rigorous procedures, cracking may occur in the later stage. For example, the following:
1. Cracking at the seam of the grey quartz vanity top: When the main installer was splicing the seam, the seam was not aligned, the upper part of the bell mouth was small, the lower part was large, the glue was not evenly spread, and more importantly, the F clamp was not used to fix it after the glue was applied, or Adding curing agent to the glue or accelerating the excessive amount of the glue will make the joints more brittle and crack when they are slightly impacted during use;
2. Cracking at the corner: Leaning against the wall too tightly without leaving shrinkage joints, the height between the two cabinets is uneven or not leveled, the front corner is opened at a right angle and the internal stress is concentrated, and the table surface is not uniformly shrunk due to external impact or temperature changes and cracks;
3. Cracks around the above grey quartz vanity top: there is no gap between the grey quartz vanity top and the basin hole, the basin hole is not polished and smooth, the corners of the basin hole are not rounded or there are serrated marks, and the table surface shrinks unevenly and cracks due to external impact or temperature changes;
4. Cracking around the furnace hole: there is no gap between the gas stove and the furnace hole, the furnace hole is not polished smooth, the four corners of the basin hole are not rounded or there are jagged marks, and the table surface is not uniformly shrunk due to external impact or temperature changes and cracks;
5. Cracks in the skirts of the above counter basins and stove holes: the load of the counter basin or stove cabinet is placed flat, when the above counter basins, the skirts of the stove holes are subjected to gravity (people stepping, stepping, etc.), etc., causing the grey quartz vanity top and stoves The skirt before the hole is cracked;
VI. Cracking of the rear water barrier: the cabinet is not level or the backing board is not leveled;
Seven. Cracks on the connecting surface of the rear water retaining edge: the glue is not firmly bonded;
8. Cracking in the center of the grey quartz vanity top: high temperature, external impact, uneven cabinets or pads, internal damage to the board, etc.; therefore, the main factor causing countertop cracking is the poor quality control of the grey quartz vanity top during processing.
Share